155-7PH/UNS S15700 Plate, Bar, Forging
Available Products
Tubus inconsutilem, Plate, Rod, Forgings, Fasteners, Pipe Fittings.
Productio signa
| Productum | ASTM |
| Vectes, denudat et profiles | A 564, A 484 |
| Plate, Sheet and Strip | A 693, A 480 |
| Forgings | A 705, A 484 |
Compositio chemica
| % | Fe | Cr | Ni | Mo | C | Mn | Si | P | S | Al |
| Min | libratum | 14.0 | 6.50 | 2.00 |
|
|
|
|
| 0.75 |
| Max | 16.0 | 7.75 | 3.00 | 0.09 | 1.00 | 1.00 | 0.041 | 0.030 | 1.50 |
Corporalia Properties
| Density | 7.81 g/cm3 |
| Exustio | 1415-1450℃ |
15-7PH Material Properties
15-7PH est praecipitatio semi-austenitica induratio incorrupta ferro magnis viribus, alta duritia et repugnantia bona corrosio.Suprema corrosio resistentiae in calore tractatae TH 1050 et RH 950 condiciones peior est quam normae ferreae durabiles immaculatae chromium serierum 400 fundatorum, non autem tam bona quam chromium-nickel-fundatum 304 chalybe immaculata.
PH15-7Mo (type 632) vexillum nationale 0Cr15Ni7Mo2Al, Iaponia SUS632, chalybeum enucleatum est reposito 2% chromii in ferro 0Cr17Ni7Al cum 2% molybdaeno.Eius proprietates fundamentales ferro 0Cr17Ni7Al similes sunt, sed altiore effectu eo melior est.In austenite statu potest sustinere varios frigorum formandos et glutinosos processus, et tum summa vi obtineri post curationem caloris;Egregiam caliditatis vim habet infra 550 .Adhibetur in fabricando partium structurarum tenuissimarum aviationum, variarum vasorum, tibiarum, fontium, membranarum valvularum, spicula navis, discorum compressorum, partium reactoralium, variarum partium structurarum chemicarum et aliarum partium.
15-7PH Status Caloris Curatio: Status, TH1050 Status, RH950 Status, CH900 Status Tres Caloris Curatio Systema
State A: Post solutionem curationis in 1050°C, aqua refrigeratio vel aeris refrigeratio.Metallographica structura ab austenite insignitur.
TH1050 status: Post solutionem curationis 1050°C, habe ad 760°C±15°C pro 90min, frigus aeris, refrigerium ad 15°C, vel locus temperatus intra 1h, habe pro 30min, deinde calor ad 565°C±10 °C, 90 min in aere, etiam ut 565°C senescit.The metallographic structure is characterised by praecipitatio martensite obdurationis.
RH950 statu: Post solutionem curationis ML°C, habe ad 955°C±15°C per 10 minuta, frigus aeris ad cella temperatura, frigus ad -73°C±6°C intra 24 horas, habe per 8 horas; deinde caloris ad 510°C±6°C, 60 minuta in refrigerio aeris habeto, etiam nota 510 senescit.The metallographic structure is characterised by praecipitatio martensite obdurationis.
CH900 statu: Post solutionem curationis ad 1050°C, frigus volubile cum 60% deformatione, calefactio ad 490°C pro 60min, refrigeratio aeris ad locus temperatus.The metallographic structure is characterised by praecipitatio martensite obdurationis.
15-7PH Mechanica Properties
Mechanica proprietatum 0Cr15Ni7Mo2Al ad locus temperatus
Robur distrahens σ (MPa): 565°C canus: ≥1210;510°C canus: ≥1323;
Conditionalis cedat vires σ0.2 (MPa): 565°C canus: ≥1097.6;510°C canus: ≥1210;
Prolongatio δ5 (%): 565°C canus: ≥17;510°C canus: ≥6;
Reductio areae (%): canus 565°C: ≥25;510°C canus: ≥20;
duritia HB: publicae A: ≤269;565°C: ≥375;510°C: ≥388;
15-7PH Material Application Areas
( 15-7PH ) 0Cr15Ni7Mo2Al chalybs immaculata late in industria chemica adhibita est.Maxime usus est varias vasculas, tibias, fontes, diaphragmata, etc.Eius corrosio resistentia superat ferrum martensiticum inactum, praecipitatio martensitica induratio ferro incorrupto et ferro incorrupto.
Diaphragmata, tabulata mellis conflata et aenea, diaphragmata aircraft, fontium, annulos retentis.Fontes facite.circulus calidus.Peripatetici accessiones sunt.Medici cultri.oleum EXERCITATIO.